Degradation of Crystal Violet Dye from Waters by Layered MnO2 and Nanocomposite-MnO2@MnFe2O4 Catalysts

Sulardaki Kristal Moru Boyasının Tabakalı MnO2 ve MnO2@MnFe2O4 Nanokompozit Katalizörleri ile Parçalanması


In this study, the removal and degradation of a basic triphenylmethane dye “crystal violet” (CV) was investi- gated by using layered MnO2 and MnO2 @MnFe2O4 nanocomposite catalysts in aqueous solutions in the presence of H2O2. The reaction was faster with the layered MnO2. The catalytic degradation of CV was traced by analyzing the degradation products using Electrospray Ionization-Quadrupole-Time-of-Flight-Mass Spectrometry (ESI-Q-ToF-MS). 4-isocyanobenzaldehyde (A) and Michler’s ketone (B) were identified as main intermediates both of which can potentially be bioremediated to mineralization products. MnO2/H2O2 thus appeared to be an encouraging catalyst system in converting CV to biodegradable fragments.

Bu çalışmada, bazik bir trifenilmetan boyası olan “kristal moru”nun (CV) sulu çözeltilerde H2O2 varlığında uzaklaştırılması ve bozunması, tabakalı MnO2 ve ayrıca MnO2 @MnFe2O4 nanokompozit katalizörler kullanılarakaraştırıldı. CV’nin bozunmasının tabakalı MnO2 yapısı ile daha hızlı gerçekleştiği görüldü. Katalitik bozunma ürünleri Elektrospray İyonlaşmalı-Dörtlü-Uçuş Zamanlı Kütle Spektrometresi (ESI-Q-ToF-MS) kullanılarak izlendi ve analiz edildi. Ana parçalanma ürünleri olarak, biyo-iyileştirme ile mineralizasyon ürünlerine dönüşebilme potansiyeli olan 4-izosiyanobenzaldehit (A) ve Michler ketonu (B) tanımlandı. Böylece, MnO2/H2O2 sisteminin CV’yi biyo-bozunabilir yapılara dönüştürebilen özendirici bir katalizör olduğu anlaşıldı.



Download Article in PDF (892.1 kB)



Feedback
  • ISSN 1303 5002
  • © 1973-2024 Hacettepe University